Abstract
Objectives. A newly designed light-cured reinforcement made from urethanemethacrylate oligomer and woven glass cloth has orthotropic anisotropy. This is produced for incorporation into the outermost position under the greatest tension in denture base resins. In this study, the flexural properties of self-, heat-, and light-curing reinforced resins were determined. Methods. The silanized glass cloth was soaked in urethanemethacrylate oligomer containing camphorquinone and 2-(dimethylamino)ethylmethacrylate. It was sandwiched between two pieces of polyethylene film and pressed to form a reinforcement sheet 0.3 mm in thickness, which was light-cured and prepared using four different surface conditions: with or without the polyethylene film and with or without a bonding agent. The reinforcement sheet was fixed in a fluorocarbon resin mold 3 mm in thickness, which was filled with self-, heat-, or light-curing resin and cured. The cured laminated plate was cut for flexural testing (40×7×3 mm 3). A three-point flexural test was carried out at a crosshead speed of 2 mm/min and a span length of 30 mm. In this study, the glass fiber content was measured at percentages by weight because it was not possible to determine accurately the volume of the various polymers. Results. The baseline flexural strengths of the self-, heat-, and light-curing resins were 76.2, 68.6, and 55.6 MPa, respectively, and these values were increased to 271.7, 216.4, and 266.5 MPa by the reinforcement sheet. The baseline flexural moduli of self-, heat-, and light-curing resins were 2.0, 2.4, and 2.1 GPa, respectively. These values were increased to 7.2, 5.1, and 6.6 GPa by the reinforcement sheet. SEM photographs revealed good impregnation of the glass fiber within the polymer matrix. Significance. The differences in the flexural strengths and flexural moduli of the control and reinforced specimens were significant ( p<0.01).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.