Abstract
Ti-rich PbZr1−xTixO3 (x = 0.65, PZT65) single crystals with the dimensions of 1 × 1 × 0.2 mm3 were grown by the self-flux method. Micron-sized ferroelectric domains were observed and characterized via piezoresponse force microscopy (PFM) and switching spectroscopy PFM. Both out-of-plane and in-plane components of polarization were obtained by detecting vertical and lateral vibrations of the PFM cantilever. The piezoresponse image examination revealed a clear lamellar domain structure due to apparent twinning and the formation of 90° domains. A negative self-polarization was observed in the studied crystals leading to the asymmetry of piezoresponse hysteresis loops and the polarization imprint. The polarization switching mechanism under the external electric field applied via a PFM tip was investigated. The 90° domain wall width was determined from the local PFM measurements and tentatively attributed to the oblique domain walls and chemical disorder. The time-dependent PFM imaging revealed a slow polarization relaxation process with a characteristic time of about 200 min.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.