Abstract
High temperature crack growth behavior is investigated over a wide range of R-ratios, frequencies, and temperatures in Alloy 800H. It is found that high R-ratio, low frequency, or high temperature can enhance creep damage and thus induce an intergranular crack growth mode. At low frequencies, the nonlinear fracture mechanics parameter, C*, is found to correlate time-dependent fatigue crack growth rate well if the applied mean stress is used in calculating C*. On the other hand, the Paris crack growth law using Keff is proven to be an adequate expression to use when fatigue (time-independent) damage dominates. These conclusions correlate well with damage mechanisms observed from sample fracture surfaces.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.