Abstract
The aim of this study was to investigate the flexural fatigue behavior of 11 packable composites. Of each material 30 rectangular samples (1.2×5×35 mm) for flexural fatigue test were prepared. The clamped fracture strength and flexural fatigue limit (FFL) of each material were determined using a custom-made fatigue machine, after storage of the samples for one month in water at 37 °C. All data were analyzed using one-way ANOVA and Bonferroni/Dunn's test for multiple comparisons ( p<0.05). Regression analysis was used to evaluate the relationship between elastic modulus (Abe et al., 2001), clamped fracture strength or FFL and inorganic filler fraction (vol%). The fracture strengths of all but two materials were in between those of the compact-filled densified composites and the microfine ones. The FFL of the packable composites tested were significantly lower than those of the compact-filled densified composites. Three of the tested materials showed even significantly lower FFL than did the microfine composites. There were statistically significant relationships between both the elastic modulus and the volumetric filler fraction ( R 2=0.974, p=1.990×10 −7). The great diversity in packable composites makes clinical assessment necessary with regard to a justified use in posterior teeth.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.