Abstract
Corrosion processes are frequent reasons of failure of materials in many applications. Results of failure analysis of the crude-oil tank after more than 30 years of service are summarized in this work. The failure was caused by two different and independent corrosion processes – corrosion in crude oil inside the tank and corrosion from concrete base under the tank. Both corrosion processes usually occur equally over the whole surface. In this case, however, both the corrosion processes occurred with distinctly higher corrosion rate in basic material alongside of heat affected zone of weld joint as well. The crack with length about 420 mm was the final result of these processes. The effect of low-cycle fatigue from filling and draining of crude oil is usually significant and was discussed as well.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.