Abstract
Nanoparticles of ZnS-AgInS2 solid solution (ZAIS) were synthesized by the thermal decomposition of (AgIn)xZn2(1-x)(S2CN(C2H5)2)4 precursors in a hot oleylamine solution. X-ray powder diffraction analyses revealed that the resulting nanoparticle powders were not a mixture of ZnS and AgInS2 but a ZnS-AgInS2 solid solution in which the fraction of ZnS was enlarged with a decrease in the value of x, that is, an increase in the content of Zn2+ in the precursors used. The energy gap of ZAIS nanoparticles could be controlled by the composition of solid solution. Intense emission was observed at room temperature, regardless of the kind of the particles, the peak wavelength of PL being blue-shifted from 720 to 540 nm with a decrease in the value of x. The highest quantum yield of ca. 24% was obtained for nanoparticles prepared with x = 0.86, which was much higher than the quantum yields reported for I-III-VI2-based semiconductor nanoparticles, such as CuInS2 and ZnS-CuInS2 solid solution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.