Facile production of three-dimensional chitosan fiber embedded with zinc oxide as recoverable photocatalyst for organic dye degradation

Abstract

Herein we report on a facile and green strategy for continuous production of chitosan-zinc oxide fibers and then compare their photodegradation performance against three organic dyes (i.e., methylene blue (MB), methyl orange (MO) and Rhodamine B, respectively) under different lights. Chitosan-zinc hydrogel fibers (CS/Zn) with different zinc loadings are obtained by direct mixing of chitosan and zinc acetate solutions using a double-syringe injection device. The as-prepared CS/Zn fibers are then immersed into glutaraldehyde (GA) and sodium hydroxide solutions, respectively, and dried at T = 50 °C. The resultant CS/ZnO/GA fibers of ca. 617 μm in diameter are characterized using X-ray diffraction (XRD), thermogravimetric analysis and field emission scanning electron microscope (FE-SEM). XRD and FE-SEM data confirm that the CS/ZnO/GA fibers consist of a large amount of hexagonal wurtzite ZnO nanorods up to 550 nm in length, and exhibit three-dimensional interconnected macroporous architecture. Photodegradation results clearly show that the CS/ZnO/GA fibers are effective for the removal of organic dyes upon UV irradiation and can be easily recovered and reused for at least 6 consecutive cycles. Unlike most reported CS/ZnO nanocomposites, the current CS/ZnO/GA fiber shows a higher adsorption of cationic MB rather than anionic MO, the mechanism of which is proposed.