Abstract
A simple and stable procedure for preparing mixed phase porous TiO2 nanotubes via an emulsion electrospinning is reported. The obtained porous TiO2 nanotubes were characterized by field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), X-ray diffraction pattern (XRD), Raman spectroscopy (RS), X-ray photoelectron spectroscopy (XPS), photoluminescence spectrum (PL) and lifetime. These TiO2 nanotubes have a highly porous structure with an average diameter of 200nm. The results show that the small grain size of the rutile crystallites in the porous TiO2 nanotubes would make more catalytic “hot spots” at the rutile/anatase interface than that at the mixed phase TiO2 nanofibers and Degauss P25 under visible light irradiation. According to the decay curve, it implies these “hot spots” would restrict electron/hole recombination and leading a longer life time of 3.11ns in this porous nanotube compared to nanofibers and Degauss P25. Thus, these “hot spots” would stabilize the charge separation and enhance the photocatalytic activity of methyl orange (MO) under visible light irradiation. This method could be extended to the fabrication of various types of highly porous nanotubes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.