Facile and Green Synthesis of CdSe Quantum Dots in Protein Matrix: Tuning of Morphology and Optical Properties

Abstract

Herein, we have demonstrated a facile and green approach for the synthesis of Cadmium selenide (CdSe) quantum dots (QDs). The process was mediated by bovine serum albumin (BSA) and it was found that BSA plays the dual role of reducing agent as well as a stabilizing agent. The QDs exhibited sharp excitonic absorption features at ~500 nm and subsequently showed reasonably good photoluminescence (PL) at room temperature. The PL is seen to be strongly dependent on the concentration of the precursors and hence, the luminescence of these QDs could be conveniently tuned across the visible spectrum simply by varying molar ratio of the precursors. It can be envisaged from the fact that a red-shift of about 100 nm in the PL peak position was observed when the molar ratio of the precursors ([Cd2+]:[Se2-], in mM) was varied from 10:5 to 10:40. Subsequently, the charge carrier relaxation dynamics associated with the different molar ratio of precursors has been investigated and very interesting information regarding the energy level structures of these QDs were revealed. Most importantly, in conjunction with the optical tuning, the nanomorphology of these nanoparticles was found to vary with the change in molar ratios of Se and Cd precursors. This aspect can provide a new direction of controlling the shape of CdSe nanoparticles. The possible mechanism of the formation as well as for the shape variation of these nanoparticles with the molar ratios of precursors has been proposed, taking into account the role of amino acid residues (present in BSA). Moreover, the QDs were water soluble and possessed fairly good colloidal stability therefore, can have potential applications in catalysis and bio-labeling. On the whole, the present methodology of protein assisted synthesis is relatively new especially for semiconducting nanomaterials and may provide some unique and interesting aspects to control and fine tune the morphology vis-à-vis, their optical properties.