Abstract
Up-conversion phosphors have attracted considerable attention because of their applications in solid-state lasers, optical communications, flat-panel displays, photovoltaic cells, and biological labels. Among them, NaYF4 is reported as one of the most efficient hosts for infrared to visible photon up-conversion of Yb3+ and Er3+ ions. However, a low-temperature method is required for industrial scale fabrication of photonic and optoelectronic devices on flexible organic substrates. In this study, hexagonal β-NaYF4: 3 mol% Yb3+, 3 mol% Er3+ up-conversion phosphor using Ca2+ was prepared by chemical solution method. Then, we synthesized a nanostructured organo-silicon compound from methyl tri-methoxysilane and 3-glycidoxy-propyl-trimethoxy-silane. The transmittance of the organo-silicon compound was found to be over 90% in the wavelength range of 400~1500 nm. Then we prepared a fluoride-based phosphor paste by mixing the organo-silicon compound with Na(Ca)YF4:Yb3+, Er3+. Subsequently, this paste was coated on polyethylene terephthalate, followed by heat-treatment at 120 °C. The visible emission of the infrared detection card was found to be at 655 nm and 661 nm an excitation wavelength of 980 nm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.