Abstract
Al2O3-coated Ba0.95Ca0.05Ti0.85Zr0.15O3 dielectric ceramics with excellent performance were fabricated by a novel aqueous chemical coating method. With this method, Al2O3 was well coated on the surface of Ba0.95Ca0.05Ti0.85Zr0.15O3 powders, resulting in homogenous microstructure, excellent dielectric and electrical properties. The specimen with an appropriate coating amount of 0.4wt% Al2O3 exhibited the most outstanding properties. The dielectric constant at room temperature could reach ~13,600, with low dielectric loss (~0.5%) and high insulation resistivity (~6.2×1011Ω·cm). DC breakdown strength was also improved to ~12.5kV/mm because of Al2O3 coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.