Fabrication of electrospun nanofibre yarn based on nylon 6/microencapsulated phase change materials

Abstract

ABSTRACTTwisted nylon 6 nanofibre yarns containing microencapsulated phase change materials (MPCMs) were fabricated via electrospinning to prepare thermal regulating nanofibre yarns. Electrospun nanofibre yarns with different contents of MPCMs including 0.375, 0.75, 1.5 and 3 wt% were prepared. The surface morphology, crystallisation and thermal properties of the yarn samples were characterised by scanning electron microscopy (SEM) and differential scanning calorimetry, respectively. SEM results showed that electrospun composite fibres and yarns had good morphology with smooth surface and the MPCMs were randomly distributed on the composite yarn surface, inside the nanofibres and between the fibres in the yarn structure. Additionally, the SEM results suggested that the average diameters of nylon 6/MPCM nanofibres decreased from 0.23 ± 0.03 µm for neat nylon 6 to a minimum of 0.10 ± 0.02 µm for composite yarn containing 3 wt% MPCM. However, nylon 6/MPCM nanofibre yarn diameter displayed a complex behaviour; the average diameters of electrospun composite yarns increased upon addition of MPCM and reached a maximum value of 165.1 ± 5.11 µm for composite yarn containing 0.75 wt% MPCM, then decreased markedly. These changes in nylon 6/MPCM nanofibres and yarn diameters have been discussed in terms of electrospinning solution properties and twist parameter. The melting enthalpy values of MPCM in the composite nanofibre yarns increased as the content of MPCMs increased up to the highest content and higher than 80% of the heat storage capacity of MPCMs was retained after electrospinning.