Abstract
Anode-supported solid oxide fuel cells (SOFC) based on gadolinia-doped ceria (GDC) are developed in this study. A carbonate co-precipitation method is used to synthesize the nano-sized GDC powders. A dense GDC electrolyte thin film supported by a Ni–GDC porous anode is fabricated by dry-pressing and spin-coating processes, respectively. In comparison with dry pressing, it is easy to prepare a thinner electrolyte film by the novel spin-coating method. Cell performance is examined using humidified (3% H 2O) hydrogen as fuel and air as oxidant in the temperature range of 500–700 °C. Cell performance is strongly dependent on the electrolyte thickness. With a porous Ni–GDC anode, a dense 19-μm GDC electrolyte film and a porous La 0.6Sr 0.4Co 0.2Fe 0.8O 3–GDC cathode, the cell exhibits maximum power densities of 130, 253, 386 and 492 mW cm −2 at 500, 550, 600 and 650 °C, respectively. It is also found that at the low operating temperature about 500 °C, the cell resistance is significantly dominated by the electrode polarization resistance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.