Organo-metal halide perovskite demonstrates a large potential for achieving highly efficient photovoltaic devices. The scaling-up process represents one of the major challenges to exploit this technology at the industrial level. Here, the scaling-up of perovskite solar modules from 5 × 5 to 10 × 10 cm2 substrate area is reported by blade coating both the CH3NH3PbI3 perovskite and spiro-OMeTAD layers. The sequential deposition approach is used in which both lead iodide (PbI2) deposition and the conversion step are optimized by using additives. The PbI2 solution is modified by adding methylammonium iodide (MAI) which improves perovskite crystallinity and pore filling of the mesoporous TiO2 scaffold. Optimization of the conversion step is achieved by adding a small concentration of water into the MAI-based solution, producing large cubic CH3NH3PbI3 grains. The combination of the two modifications leads to a power conversion efficiency of 14.7% on a perovskite solar module with an active area of 47 cm2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.