Abstract
A new process termed here as remelting and sedimentation (RAS) was developed to produce functionally graded Al/SiC composites with a smooth concentration gradient of SiC particles along the height of samples, as opposed to a step change. For this purpose, first settling velocities of different-sized SiC particles in aluminum A356 melt were measured, and the results exhibited a reasonably good agreement with those predicted via the modified Stokes law. Then slices of particulate Al/SiC composites with different SiC contents of 5, 10, 15, and 20 vol.% were stacked in a cast iron mold and heated at 650 °C resulting in remelting and unification of the different composite parts. Considering the preliminary settling experiments, the composite slurry was held at this temperature for three different times to investigate the optimum holding time for obtaining a smooth gradient of SiC concentration along the height of the sample. After quenching, the samples were sectioned and subjected to metallographic studies and hardness measurements. The results confirmed that holding the melt for 60 s provides sufficient settling and redistribution of SiC particles and results in successful production of a functionally graded material.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.