Abstract
Cellulose acetate (CA) nanofiber membranes incorporated with diatomite (DE) were prepared by electrospinning to produce electrospun nanofiber membranes with high specific surface area and high porosity with fine pores. When the DE percentage increased from 0 to 30%, the water contact angle (WCA) of the membranes increased from 86.21° to 118.44°, indicating that neat CA nanofibers were more hydrophilic than CA/DE nanofibers and had a better wetting tendency. CA, CA-10DE, and CA-20DE nanofiber membranes showed a mean flow pore size (MFP) of 2.941, 2.681, and 2.408 μm, respectively, with narrow pore size distributions. However, the CA-30DE nanofiber membrane showed a smaller MFP size of 0.5014 μm. CA nanofibers were produced in the range of 206.31 to 281.13 nm. The dye removal ability of these membranes was tested using an aqueous solution of C.I. Reactive Red 141.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.