Abstract
Stacking of poly(3-alkylthiophene)s P3RThs and poly(4-alkylthiazole)s P4RTzs has been studied. Light scattering analysis indicates that head-to-tail (HT) type HT-P3HexTh (R = n-C6H13) gives a degree of depolarization (ρv) of 0.26 in CHCl3, which reveals that HT-P3HexTh takes a stiff structure even in the good solvent. Addition of CH3OH to CHCl3 solutions of HT-P3HexTh and head-to-head (HH) type HH-P4HepTz (R = n-C7H15) leads to π-stacking of the polymer molecules to form stable colloidal particles. The light scattering analysis of the colloidal solution of HT-P3HexTh in a 2:1 solution of CHCl3 and CH3OH reveals that HT-P3HexTh is aggregated in a parallel style. Results of filtration experiments using membranes with 0.20 and 0.02 μm pores agree with the degree of the aggregation. P3HexThs with irregular structures (P3HexTh (Fe) and P3HexTh (Ni) with HT/HH ratios of about 7/3 and 1/2, respectively) show a weaker trend to aggregate; however, P3HexTh (Fe) is considered to stack in a surface region of a stretc...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.