Abstract
3D printing technology has drawn considerable attention in various applications due to its appealing features such as freedom of design, quick fabrication, automation, no solvent discharge, and less environmental issues. The feasibility of using 3D printed (3DP) membranes in membrane distillation (MD) was explored for the first time. Polyamide (PA) membranes were printed in a laser sintering (LS) technology and further coated with thin poly(vinylidene fluoride) (PVDF) layers to reduce the pore size. Results show that the PVDF layers could effectively reduce the membrane pore size from 15.9 ± 5.3 μm to 1.0–2.5 μm. Additionally, due to the granular and rough surface of the 3DP membranes, the hydrophobicity of the composite membranes (100°–130°) is greater than for the PVDF membranes manufactured on the flat substrates (~70°). However, the great thicknesses of the PA membranes of 359.6 ± 38.9 μm lead to relatively thick composite membranes. The PVDF@3DP membranes show DCMD fluxes of 5–10 kg/(m2·h) at a temperature difference of 40 °C. The overall results indicate that the 3DP substrate significantly affect the composite membrane properties and MD performance. Therefore, improving the printed membrane's porosity and thickness will be advantageous to prepare membranes with quick fabrication and less solvent discharge.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.