Abstract
Magnesium oxide (MgO) thin films, both pure and zinc (Zn) doped, were fabricated on soda lime glass substrates using ultrasonic spray pyrolysis. Zn was introduced at concentrations of 0.5 %, 1 %, 2 %, 4 %, and 8 %. The effects of these doping levels on the films' structural, morphological, optical, and H2 gas sensing properties were studied using XRD, SEM, EDAX, UV–vis spectroscopy, PL spectroscopy, gas sensing measurements, and XPS. The films showed a cubic crystal structure without secondary phases, and grain sizes generally decreased with doping. Morphological changes in nanocrystal shapes were noted due to impurities. Optimal doping enhanced MgO's absorbance, with a slight increase in bandgap. The PL spectra showed increased luminescent emissions with higher doping, due to defects from Zn ions. Pure films were responsive to H2 gas, while Zn-doped samples showed weaker responses. The XPS confirmed the expected chemical compositions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.