Abstract
Dilatometric curves of iron-copper compact made from elemental or pre-alloyed powder were compared in order to study its expansion mechanism. The compacts from a mixture of elemental iron and copper powders showed the maximum expansion at the copper powder content of 7.44mass% and at the sintering temperatures above the copper melting-point. In the case of the compacts from a mixture of iron pre-alloyed powder of (Fe- 3.44mass%Cu) and copper powder, the maximum expansion which is lower than the former case was obtained at the additive copper powder content of 4.00mass%. But the compact from a mixture of iron pre-alloyed powder of (Fe-7.18mass%Cu) and copper powder showed only shrinkages at any additive copper powder content. The penetration of liquid copper into the interstices between solid grains was observed in all sintered compacts. The iron-copper compacts containing the same content of copper powder showed a very different expansion behavior depending on the amount of copper content in the starting iron raw powder.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.