Abstract
Nickel-based superalloys have a wide range of usage area such as gas turbines, nuclear reactors, generators. They are especially preferred in areas where mechanical strength and corrosion resistance are important. Hot corrosion is a highly corrosive type of damage in high temperature applications. In hot corrosion, molten salts easily react with reactive components, causing premature damage to the workpieces. In this study, Inconel 718 was subjected to hot corrosion tests as a nickel-based superalloy. 50% V2O5-50% Na2SO4 mixtures were used as corrosion salt. Cyclic and isothermal hot corrosion tests were carried out at 900 ° C for 18 hours. Corrosion products and microstructural changes formed in Inconel 718 were characterized by scanning electron microscopy (SEM), SEM-Energy Dispersive X-Ray (EDX), SEM-mapping and X-Ray Diffraction (XRD) analysis after hot corrosion tests. At the end of the isothermal and cyclic hot corrosion tests, Inconel 718, which has been subjected to cyclic hot corrosion, has been found to be more affected by the damage. Similar results were observed in terms of the corrosion products and the damage mechanism.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.