Abstract
Irradiation temperature is one of the most important parameters which determine the evolution of structural materials’ properties. In this study, the evolution of vacancy-type defects and hardening behaviors of T91 steel induced by Fe-ion irradiation at different temperatures were investigated. The 1.625MeV Fe ions were implanted in T91 to the fluence of 2.5×1015ions/cm2 at temperatures from room temperature (RT) to 550°C. After irradiation, the samples were analyzed by positron annihilation spectroscopy (PAS) and nano-indention technology (NIT). It was found that the sample irradiated at RT possessed the largest concentration of vacancy-type defects. At higher temperatures, the variation of vacancy-type defects concentrations were in a trend of Cv550°C<Cv300°C<Cv450°C. All the samples were hardened to different extents after irradiation. The hardness values increased initially and decreased afterward with the increasing temperatures, and the peak hardening is present at 300°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.