Abstract
In this study, microstructural and electrochemical behavior of a UNS S31803 duplex stainless steel aged at 475°C were investigated. Hardness values increased with aging at 475°C and evidence of alpha prime (α′) phase formation was confirmed by transmission electron microscopy analysis. Double loop electrochemical potentiokinetic reactivation measurements in a 2 M H2SO4 + 0.5 M NaCl + 0.01 M KSCN solution showed an increase in the degree of sensitization values, mainly for the sample aged for 360 h at 475°C. Moreover, the results suggest that α′ phase formation occurred via spinodal decomposition mechanism.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.