Abstract
Abstract This study carried out mechanical tests and microstructural characterizations of several 9Cr and 11Cr-ODS tempered martensitic steels. From those results, the appropriate chemical composition range of 11Cr-ODS tempered martensitic steel was discussed from the viewpoint of high temperature strength improvement. It was shown that the residual α-ferrite fraction in 11Cr-ODS steel was successfully controlled to the same level as the 9Cr-ODS steel, which has excellent high temperature strength, by selecting the chemical compositions on the basis of the multi-component phase diagram. The tensile strength decreased with decreasing W content from 2.0 to 1.4 wt%. On the other hand, creep strength at 973 K did not degrade by the decreasing W content. Both tensile strength and creep strength increased with increasing population of the nano-sized oxide particles. Small angle X-ray scattering analysis revealed that titanium and excess oxygen contents were key parameters in order to improve the dispersion conditions of nano-sized oxide particles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.