Evaluation of liquid metal embrittlement of stainless steel 304 by cadmium and cadmium-aluminum solutions

Abstract

The susceptibility of stainless steel 304 (SS304) to liquid metal embrittlement (LME) by cadmium (Cd) and cadmium-aluminum (Cd-Al) solutions was examined as part of a failure evaluation for SS304-clad cadmium reactor safety rods which had been exposed to elevated temperatures. The safety rod test data and destructive examination of the specimens indicated that LME was not the failure mode. The available literature data also suggest that austenitic stainless steels are not particularly susceptible to LME by Cd or Cd-Al solutions. However, the literature data is not conclusive and an experimental study was therefore conducted to examine the susceptibility of SS304 to LME by Cd and Cd-Al solutions. Temperatures from 325 to 600°C and strain rates from 1 × 10 −6 to 5 × 10 −5 s −1 were of interest in this evaluation. Tensile tests carried out in molten Cd-Al and Cd solutions over these temperatures and strain rates with both smooth bar and notched specimens showed no evidence of LME. U-bend tests conducted in liquid Cd at 500 and 600°C also showed no evidence of LME. It is concluded that SS304 is not subject to LME by Cd or Cd-Al solutions over the range of temperatures and strain rates of interest.