Abstract
A new novel cored wire for producing FeCrAl/WC intermetallic coating by arc spraying was developed. The erosion wastage at high temperature of the coating was researched with different impingement angles and temperatures. The results indicated that impingement angle and temperature greatly affected erosion wastage of the coating. At the same time, when impingement angle was 90°, different temperature had a little effect on the erosion wastage. And when temperature was 650°C, different impingement angle had a little effect on the erosion wastage too. As compared with water wall tube material (G20 steel) of power station boiler, the erosion resistance at high temperature of the coating was higher. The erosion resistance rate of the coating was 1.94~2.89 times of that of G20 steel when temperature was 650°C and particle was polygonal silica. The results indicated that erosive condition of high temperature flue gas and fly ash mixture in boiler tube of pulverized coal fired power station could be solved with the FeCrAl/WC coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.