Abstract
Isobam is widely used for fabricating ceramics through spontaneous gelation and has attracted considerable interest. However, the disadvantage of the Isobam system is the low gelation strength. The effects of suitable additives and the mechanism by which they effectively enhance the green body strength and the rheological behavior of an aluminum nitride (AlN) slurry with 50 vol% solid loading were investigated using polyethyleneimine (PEI), hydantoin epoxy resin, and trimethylolpropane triglycidyl ether (TMPGE). Results showed that the additives acted as both dispersants and cross-linkers in the AlN suspension using the Isobam gelling system. The flexural strength of the AlN green body increased by 42%, 204%, and 268% with the addition of 1 wt% PEI, 1 wt% hydantoin epoxy resin, and 0.5 wt% TMPGE, respectively. After sintering at 1700 °C, the AlN ceramic with 0.5 wt% TMPGE had flexural strength and thermal conductivity of 235 MPa and 166.44 W/(m·K), respectively, showing superior performance to the ceramics without additives.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.