Abstract
ABSTRACTIn this paper, we report a method of increasing fracture toughness (KIC) and strain energy release rate (GIC) of vinyl ester matrix by adopting a dual reinforcement strategy. Reinforcements were carbon nanotubes (CNT) and graphene nanoplatelets (GNP). Both categories of nanoparticles were functionalized with COOH. The idea was to enhance crack bridging and interface sliding with CNT inclusions, given their high aspect ratio. In addition, promote crack-tip blunting and cross-linking density with GNP inclusions, due to their platelet structures. Both KIC and GIC were measured using ASTM D5045-14. An exhaustive experimental study revealed an optimum loading of both nanoparticles to be 0.25 wt% CNT and 0.5 wt% GNP, based on the highest combination of KIC and GIC values. We observed that stress intensity factor, KIC, of neat vinyl ester increased by 43% from 1.14 to 1.62 MPa*(m½). Meanwhile, the improvement in GIC was even greater with an increase of 65%, i.e., from 370 to 610 J/(m2). Differential scanning calorimetry (DSC) studies showed a discernible shift in glass transition temperature (Tg) from 123 to 128°C. The slight temperature increase was similar in thermogravimetric analysis (TGA). We observed the maximum thermal decomposition temperature (Tp) increase from 410 to 414°C, as was evident in the derivative TGA (DTG) curves.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.