Abstract
A homogeneously ultrafine-grained (UFG) Cu-38 Zn alloy with an average grain size of 0.64 μm is successfully fabricated by equal channel angular processing (ECAP), which exhibits a significantly enhanced strength-ductility synergy. The strength enhancement can be attributed to grain refinement and dislocation strengthening. After annealing the ECAP processed alloy at 300 °C for 30 min, a further enhanced strength with almost unchanged ductility was achieved. This unusual annealing strengthens is associated with the solute/impurity segregation and precipitations inside the grains.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.