Abstract
This research was conducted by the application of high-pressure torsion (HPT) to Al-X wt pct Ag alloys (X = 5, 11, 20). Grain refinement was achieved to the size of ~300 nm after HPT processing at room temperature. The aging behavior of the alloys after HPT processing was investigated using Vickers microhardness measurement, tensile testing, scanning electron microscopy, and transmission electron microscopy. This study confirms the dual effect of grain refinement and fine precipitation on the enhancement of the strength. It is also shown that at peak-aged condition, the tensile strength is enhanced while maintaining considerable ductility.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.