Enhancement of effluent degradation by zinc oxide, carbon nitride, and carbon xerogel trifecta on brass monoliths.

Abstract

In recent years, heterogeneous photocatalysis has emerged as a promising alternative for the treatment of organic pollutants. This technique offers several advantages, such as low cost and ease of operation. However, finding a semiconductor material that is both operationally viable and highly active under solar irradiation remains a challenge, often requiring materials of nanometric size. Furthermore, in many processes, photocatalysts are suspended in the solution, requiring additional steps to remove them. This can render the technique economically unviable, especially for nanosized catalysts. This work demonstrated the feasibility of using a structured photocatalyst (ZnO, g-C3N4, and carbon xerogel) optimized for this photodegradation process. The synthesized materials were characterized by nitrogen adsorption and desorption, X-ray diffraction (XRD), and diffuse reflectance spectroscopy (DRS). Adhesion testing demonstrated the efficiency of the deposition technique, with film adhesion exceeding 90%. The photocatalytic evaluation was performed using a mixture of three textile dyes in a recycle photoreactor, varying pH (4.7 and 10), recycle flow rate (2, 4, and 6 L h-1), immobilized mass (1, 2, and 3mgcm-2), monolith height (1.5, 3.0, and 4.5cm), and type of radiation (solar and visible artificials; and natural solar). The structured photocatalyst degraded over 99% of the dye mixture under artificial radiation. The solar energy results are highly promising, achieving a degradation efficiency of approximately 74%. Furthermore, it was possible to regenerate the structured photocatalyst up to seven consecutive times using exclusively natural solar light and maintain a degradation rate of around 70%. These results reinforce the feasibility and potential application of this system in photocatalytic reactions, highlighting its effectiveness and sustainability.