Abstract
An in situ formed intermetallic phase/bulk metallic glass composite with high strength and good plasticity was fabricated by casting Zr55.0Cu29.0Ni8.0Al8.0 melts. In situ formed tetragonal structured (Zr,Ni,Al)2(Cu,Ni,Al) intermetallic particles with a hardness of 9.6±0.3 GPa improve the fracture strength of the composite. Micrographs of the fractured samples reveal that the shear band spacing is smaller than the intermetallic particles, indicating that they can effectively block shear band propagation before catastrophic fracture.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.