Abstract
A 50 nm-thick Co film has been grown either on the free surface (surface roughness, ∼6 nm) or on the wheel-side surface (surface roughness, ∼147 nm) of Co84.55Fe4.45Zr7B4 amorphous ribbons. A comparative study of the giant magnetoimpedance (GMI) effect and its field sensitivity (η) in the uncoated and Co-coated ribbons is presented. We show that the presence of the Co coating layer enhances both the GMI ratio and η in the Co-coated ribbons. Larger values for GMI ratio and η are achieved in the sample with Co coated on the free ribbon surface. The enhancement of the GMI effect in the Co-coated ribbons originates mainly from the reduction in stray fields due to surface irregularities and the enhanced magnetic flux paths closure. These findings provide good guidance for tailoring GMI in surface-modified soft ferromagnetic ribbons for use in highly sensitive magnetic sensors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.