Abstract
This paper reports that the nano-sheet carbon films (NSCFs) were fabricated on Si wafer chips with hydrogenmethane gas mixture by means of quartz-tube-type microwave plasma chemical vapour deposition (MWPCVD). In order to further improve the field emission (FE) characteristics, a 5-nm Au film was prepared on the samples by using electron beam evaporation. The FE properties were obviously improved due to depositing Au thin film on NSCFs. The FE current density at a macroscopic electric field, E, of 9 V/μm was increased from 12.4 mA/cm2 to 27.2 mA/cm2 and the threshold field was decreased from 2.6 V/μm to 2.0 V/μm for Au-coated carbon films. A modified F-N model considering statistic effects of FE tip structures in the low E region and a space-charge-limited-current effect in the high E region were applied successfully to explain the FE data of the Au-coated NSCF.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.