CoFe2O4 nano-particles with average size of ∼40nm were synthesized via the chemical coprecipitation method. PAMANH4 was used as dispersant to improve the stability of aqueous suspensions. Zeta potential and sediment volumes were tested to study the effects of pH and dispersant amounts on the stability of suspensions. The most stable suspension was obtained when using 0.6wt.% PAMANH4 as dispersant at pH=10. Conductivity results showed that thoroughly dispersed suspensions were formed after being ultrasonic agitated for 30min. CoFe2O4 films on Al2O3/Pt substrates fabricated via EPD sintered at 1250°C exhibited preferentially oriented structure. The XRD analyses showed (220) and (511) were the preferential orientations. Anisotropy was also observed in magnetic hysteresis loops. Stronger ferromagnetic effect was observed in the in-plane orientation, with saturation magnetization of ∼290emu/cm3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.