Abstract
The structural, magnetic, and electronic structural properties of Ni0.2Cd0.3Fe(2.5-x)Al(x)O4 ferrite nanoparticles were studied via X-ray diffraction (XRD), transmission electron microscopy (TEM), DC magnetization, and near-edge X-ray absorption fine-structure spectroscopy (NEXAFS) measurements. Nanoparticles of Ni0.2Cd0.3Fe(2.5x)Al(x)O4 (0 < or = x < or = 0.4) ferrite were synthesized using the sol-gel method. The XRD and TEM measurements showed that all the samples had a single-phase nature with a cubic structure, and had nanocrystalline behavior. From the XRD and TEM analysis, it was found that the particle size increases with Al doping. The DC magnetization measurements revealed that the blocking temperature increases with increased Al doping. It was observed that the magnetic moment decreases with Al doping, which may be due to the dilution of the sublattice by the doping of the Al ions. The NEXAFS measurements performed at room temperature indicated that Fe exists in a mixed-valence state.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.