Abstract
Patterned Nafion 212 membrane prepared by electron beam lithography (EBL) coupled with dry etching was tested for DMFC applications. Pristine, O2 blanket-etched, and electron beam exposed Nafion 212 test cells were also prepared and compared. Several parameters including in-plane conductivity, methanol crossover, I–V characteristics, and through-plane ohmic resistance were evaluated. The patterned membrane had the best combination of properties, benefiting from the exposure to electron beam and interfacial area enlargement as evidenced by its superior power density. The maximum power densities were 29.3, 32.5, 48.2, and 63.1 mW cm−2 for the pristine, exposed, O2 blanket-etched, and patterned membrane respectively. A Nafion 117 membrane test cell was also compared. While it exhibited reduced methanol crossover, it also had higher ohmic resistance and Tafel slope. The patterned Nafion 212 provided a 25% increase in power density compared to the N117 membrane.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.