Abstract
Pretreated Mg-Li alloy sheets were pre-plated in a NiCO 3·2Ni(OH) 2·4H 2O solution to form a thin Ni-P alloy film and then plating in a NiSO 4·6H 2O solution was carried out to obtain a protective coating. The surface morphology, structure and corrosion resistance of the coating were studied. The results showed that a flat, bright and compact plating layer, which was integrated into the matrix metal, was obtained. The P content of the Ni-P coating reached 13.56% (mass fraction). The hardness value of the Ni-P coating was about HV 549. The polarization curve showed that the corrosion potential of the Ni-P coating reached −0.249 V (vs SCE). A long passivation region was found on the polarization curve, and this phenomenon indicated that the coating has an excellent anti-corrosion property.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.