Abstract
AbstractWafer bonding of β‐Ga2O3 and N‐polar GaN single crystal substrates is demonstrated by adding ZnO as a “glue” interlayer. The wafers are fully bonded such that Newton rings are not observed. Temperature‐dependent current‐voltage (I–V) measurements are conducted on the as‐bonded Ga2O3/ZnO/N‐polar GaN test structure and after annealing at 600 °C and 1100 °C. The impact of post‐annealing temperature on the electrical and structural characteristics of the bonded samples is investigated. A consistently ohmic‐like characteristic is obtained by annealing the bonded wafers at 1100 °C in N2, which is in part due to crystallization of ZnO and diffusion of Ga into ZnO which makes it n‐type doped. The wafer bonding of β‐Ga2O3 and GaN achieved in this work is promising to combine the material merits of both GaN and Ga2O3 targeting breakthrough high‐frequency and high‐power device performances.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.