Abstract
The pressure behavior of Raman frequencies and line widths of crystalline core-amorphous shell silicon nanowires (SiNWs) with two different core-to-shell ratio thicknesses was studied at pressures up to 8 GPa. The obtained isothermal compressibility (bulk modulus) of SiNWs with a core-to-shell ratio of about 1.8 is ∼20% higher (lower) than reported values for bulk Si. For SiNWs with smaller core- to-shell ratios, a plastic deformation of the shell was observed together with a strain relaxation. A significant increase in the full width at half-maximum of the Raman LTO-peak due to phonon decay was used to determine the critical pressure at which LTO-phonons decay into LO + TA phonons. Our results reveal that this critical pressure in strained core−shell SiNWs (∼4 GPa) is different from the reported value for bulk Si (∼7 GPa), whereas no change is observed for relaxed core−shell SiNWs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.