Abstract
Nowadays high entropy carbides (HECs) are an important group of advanced ceramics. They are composed by at least by five transition metals (TMs) in nearly equiatomic proportion and disordered distributed in the cationic sublattice of face centered cubic structures, with carbon atoms in the octahedral interstitial voids, with general formula (TM1,TM2,TM3,TM4,TM5)C. These HECs belong to the recent novel group of ultra-high temperature ceramics (UHTCs), with superior properties in comparison with the constituent binary carbides. However, the synthesis of those HECs can be modified to develop high entropy carbonitrides, HECNs, where the C are partially substituted by N, to form a solid solution in the anionic sublattice, with expected improved properties as UHTCs, but they are in an incipient state of development. Here, we report the synthesis and deep characterization of a non-previously obtained Hf0.2Nb0.2Ta0.2V0.2Zr0.2C0.5N0.5 HECN, via a facile, single step and reproducible solid-gas reaction mechanosynthesis route. The synthesis was successfully completed in a planetary ball mill device, after 2h of milling time, at 400 rpm and using a ball-to- powder ratio of 60:1 in a pure N2 atmosphere at room temperature. The as-synthesized HECNs powdered showed nanostructured morphology and outstanding high-temperature oxidation resistance up to 1500 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.