Efficient MRI labeling of endothelial progenitor cells: Design of thiolated surface stabilized superparamagnetic iron oxide nanoparticles

Abstract

The aim of this study was to design thiolated surface stabilized superparamagnetic iron oxide nanoparticles (TSS-SPIONs) for efficient internalization with high MRI sensitivity. TSS-SPIONs were developed by chelation between thiolated chitosan–thioglycolic acid (chitosan–TGA) hydrogel and iron ions (Fe2+/Fe3+). Likely, unmodified chitosan hydrogel SPIONs (UC-SPIONs) and uncoated SPIONs were used as control. Moreover, TSS-SPIONs were investigated regarding to their iron core size, hydrodynamic diameter, zeta potential, iron contents, molar relaxivities (r1 and r2), and cellular internalization. TSS-SPIONs demonstrated an iron oxide core diameter (crystallite size by XRD) of 3.1±0.02nm, a hydrodynamic diameter of 94±20nm, a zeta potential of +21±5mV, and an iron content of 3.6±0.9mg/mL. In addition, internalization of TSS-SPIONs into human endothelial progenitor cells (EPC) from umbilical cord blood was more than threefold and 17-fold higher in contrast to UC-SPIONs and SPIONs, respectively. With twofold lower incubation iron concentration of TSS-SPIONs, more than threefold higher internalization was achieved as compared to Resovist®. Also, cell viability of more than 90% was observed in the presence of TSS-SPIONs after 24h. The molar MR relaxivities (r2) value at 1.5T was threefold higher than that of Resovist® and demonstrated that TSS-SPIONs have the potential as very effective T2 contrast-enhancement agent. According to these findings, TSS-SPIONs with efficient internalization, lower cytotoxicity, and high MRI sensitivity seem to be promising for cell tracking.