Abstract
The electrochemical behaviour of X52 steel in the presence of sulphide at 40 °C in a CO 2 environment was investigated using the methods of linear polarization resistance (LPR), potentiodynamic sweep, electrochemical impedance spectroscopy (EIS). In addition, the surface of X52 steel was also studied using scanning electron microscopy (SEM). The results showed that the corrosion rate of X52 steel increased with increasing concentration of sulphide ion. Potentiodynamic curve showed that there were changes in cathodic branch due to the change in the nature of cathodic reaction in the presence of sulphide ion. EIS analysis showed the higher sulphide ion concentration, the higher adsorbed species on the steel surface that contributed in the cathodic reaction. Furthermore, SEM results showed crevices on the scale which indicated pitting tendency in sulphide ion solutions. The less protective film, probably mackinawite, also contributed to the increase of corrosion rate in the presence of sulphide ion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.