Abstract
The effects of sintering temperature on microstructure and dielectric properties of Ce doped SrTiO3 were investigated. The dielectric properties are strongly depend on sintering temperature, the sample sintered at 1520 °C exhibits a colossal permittivity about 7000 at 1 kHz while relative permittivity of the sample sintered at 1380 °C is 770. Further investigations demonstrate that all the samples belong to Pm3¯m space group and without secondary phase. The lattice parameter decrease with the increase of sintering temperature while the mean grain size of SCT (Sr0.985Ce0.01TiO3) ceramics are increased. Higher sintering temperature helps to improve the dielectric properties which can be attribute to defect clusters (e.g. oxygen vacancies, Ti3+/Ti4+ etc.), however the defects are more likely to become carriers in high electric field which can increase the conductivity and leakage current. With the increase of sintering temperature, the conductivity activation energies, breakdown strength and energy storage density of the samples are decreased.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.