Abstract
La modified Pb(Mg1/3Nb2/3)O3-PbTiO3 (PLMNT) transparent electro-optic (EO) ceramics with pure perovskite phase were fabricated by the uniaxial hot-press sintering method. An improved hot-press sintering technique with varied atmosphere was proposed to eliminate the pore defects. It consists of four stages: 1) sintering at a relatively low temperature (800°C) in the vacuum atmosphere first, and then in the pure O2 atmosphere; 2) sintering in a pure O2 atmosphere at high temperature by uniaxial hot-press method; 3) replacing the O2 atmosphere with CO2 gas to eliminate the residual closed pores; 4) finally exchanging CO2 atmosphere with pure O2 gas to eliminate the oxygen vacancies. The research results certified that the thermal treatment in the vacuum atmosphere and CO2 atmosphere could eliminate the residual closed pores and improve the transmittance of the PLMNT transparent ceramics effectively. By the improved hot-press sintering technique, the optical transmittance of the polished PLMNT transparent ceramics with a thickness of 0.35mm increases from 61% to 64% at 632.8nm. The reasonable explanation was given about the mechanism of the improvements of this sintering technique.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.