Abstract
Microstructural instabilities associated with the precipitation of refractory-rich topologically-close-packed (TCP) phases within the microstructure of advanced Ni-base single-crystal superalloys were quantified in two nominally identical alloys with and without additions of Ru. Differences in the microstructural kinetics associated with the formation of TCP precipitates in these experimental single-crystal superalloys enabled the influence of Ru to be assessed. Detailed microstructural investigations were carried out on specimens subjected to prolonged isothermal exposures at elevated temperature. Even after 1000 hours at temperatures in excess of 1100 °C, the microstructure of the Ru-bearing alloy was highly resistant to the formation of TCP phases. Transmission electron micro-analysis (TEM) coupled with X-ray diffraction (XRD) was used to identify the characteristic crystal structures of the TCP precipitates in both alloys as being primarily the orthorhombic P and tetragonal σ phase. The sluggish precipitation kinetics of TCP phases in the Ru-bearing single-crystal Ni-base superalloy prevents the breakdown of the parent γ-γ′ microstructure and greatly enhances the high-temperature creep characteristics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.