Abstract
This paper presents the changes in mechanical properties and microstructure of aluminium alloy A356 that undergoes cooling slope casting. The alloy was cut into small cubes with an estimated weight of 400g before it was heated in a crucible induction casting machine. The temperature was set to 880 oC with a heating rate of 15 oC per min. Then, the metal was cooled to 620 oC until it turns to a semisolid, before pouring into a stainless steel mould through a 250 mm long and 60o cooling slope before it was cooled to room temperature. For the thixoforming experiments, the liquid fraction was between 30% and 50%, with various semisolid temperatures (583 oC-585 oC). The ram speed and die temperature were 85 mm/s and 200 oC, respectively. The microstructure and mechanical properties of rheocast feedstock in T6 condition were determined and compared with the metal without any heat treatment, rheocast and thixoformed alloy. It was found that thixoformed metal had the highest ultimate tensile and yield strength with reduced ductility. The microstructures are rosette, near globular and spherical, and were obtained in rheocast and thixoformed alloys, respectively. The α-Al grains were larger at higher semisolid temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.