Abstract
We studied the effect of anisotropic pore morphology on the fatigue behavior and fracture surface of lotus-type porous copper, which was fabricated through unidirectional solidification in pressurized hydrogen and argon atmospheres. The fatigue strength at finite life is closely related to the pore morphology. The fatigue strength decreases with increasing porosity, and the strength depends on applied-stress direction. The fatigue life is the longest in the direction parallel to the longitudinal axis of cylindrical pores. The fatigue strength at finite life is proportional to the ultimate tensile strength and can be expressed by a simple power-law formula. Anisotropic pores affect the fracture surface of lotus copper; crack-initiation site depends on applied-stress direction, and the anisotropic shape pores affect the direction of crack propagation and final fracture surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.