Abstract
In order to improve the experimental evidence of hotoinitiator, the effects of various dose of photoinitiator on mechanical properties of nanohydroxyapatite composite were investigated. According to the light initiating system, CQ and DMAEMA accounted for 0.8wt％, 1.0wt％, 1.2wt％ of total resin matrix, respectively. And then NHA processed by KH-570 was mixed with resin matrix in the ratio of 55:45. Then three groups （A, B, and C） of light-cured nanohydroxyapatite composites were prepared. Karuisima composite resin was used as control group D. The cured depth, compressive strength, and flexural strength were determined in each group. The results showed that as the ratio of photoinitiator increased, the cured depth increased, while the mechanical function declined. In group B, there were no significant differences in compressive strength, and flexural strength as compared with control group,P>0.05. It is suggested that the quantity of CQ and DMAEMA in resin matrix were 1.0wt% respectively, the new light-cured nanohydroxyapatite composite has good qualities in both cured depth and mechanical property.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.