Effects of La2O3 Content and Rolling on Microstructure and Mechanical Properties of ODS Molybdenum Alloys

Abstract

In order to study the effects of La2O3 content and rolling on microstructure and mechanical properties of Mo-La2O3 alloys, Mo-0.5% (1%) La2O3 alloys were prepared by liquid-solid doping technique, subsequently rolled either by a single-direction rolling or a cross-rolling. As a result, three different materials were prepared for this study. After being annealed at 1800 °C, the single-directionally rolled Mo-1% La2O3 alloy shows the best mechanical properties in terms of strength, hardness, and sagging deformation among the three materials. This is attributed to the observation that the alloy is only recovered with a microstructure of subgrains and dislocations. The single-directionally rolled Mo-0.5% La2O3 exhibits the worst mechanical property among the three materials. In this material, coarse grains, but no subgrains and dislocations, can be observed after annealing, indicating that it is fully recrystallized. For the cross-rolled Mo-1% La2O3 alloy, grains of dispersed sizes, but no dislocations, are visible after annealing, implying that this alloy is partially recrystallized. Accordingly, the mechanical property of this material is in between the other two materials. Thus, the mechanical properties of the three materials can be well understood based on OM, SEM, and TEM results. Overall, the single-directionally rolled Mo-1% La2O3 alloy possesses good mechanical properties and is more suitable for high-temperature applications.